Photocentric
Daylight Magna High Draft
Standard/Prototyping
Ultra-thick layer (350μm) draft printing, large scale concept models; LC Magna
Full specifications
Mechanical
- Tensile strength
- 38 MPa
- Elongation at break
- 8 %
- Flexural strength
- 58 MPa
- Flexural modulus
- 1500 MPa
- Izod impact (notched)
- 18 J/m
- Shore hardness
- 78D
- Compressive strength
- 55 MPa
Thermal
- HDT @ 0.45 MPa
- 56 °C
- HDT @ 1.82 MPa
- 42 °C
- Glass transition
- 58 °C
- Max service temp
- 45 °C
Curing & print
- Viscosity @ 25°C
- 210 cP
- Cure wavelength
- 460nm (Daylight) nm
- Post-cure
- 30 min UV chamber
- Shrinkage / accuracy
- 1.50%
- Water-washable
- No
Physical
- Density
- 1.11 g/cm³
- Available colors
- Grey
- Biocompatibility
- Fast draft printing